The service life of alumina wear-resistant ceramic plates is as follows:

The service life of wear-resistant ceramics is not only related to their own quality, but also to external factors, mainly including particle size, hardness, friction mode, environment, load, scouring speed, temperature, and time. Generally speaking, the smaller the particle size, the lower the concentration, the smaller the erosion speed and angle, and the longer the service life of wear-resistant ceramic plates. In the networked management of slag powder production lines, the specific surface area of fine powder is generally 420-450m2/kg, the concentration is generally 350g/Nm3, the speed is generally 28-30m/s, the scouring angle is generally 30 ° C, and 20mm wear-resistant ceramic sheets can be used for 8-10 years. Raw material mill and clinker mill are easier to grind than slag mill. The service life of wear-resistant ceramic parts with the same thickness can reach more than 10 years.